2%NiCrMo Steel Single Melted or Vacuum Arc Remelted (VAR)
Features & Benefits Chemical Composition (Wt %)
- High strength (1800 MPa)
- Good ductility
- Resistant to shock
- Excellent transverse properties in VAR material
Applications
- Aircraft landing gear component
- Gears
- Con Rods
Min | Max | |
---|---|---|
C | 0.38 | 0.43 |
Si | 0.15 | 0.35 |
Mn | 0.65 | 0.90 |
P | - | 0.010 |
S | - | 0.010 |
Cr | 0.70 | 0.90 |
Mo | 0.20 | 0.30 |
Ni | 1.65 | 2.00 |
Supply Condition & Availability Heat Treatment
Supplied annealed, normalised or Quench and double temper. normalised and tempered
Also available untreated for forging
Longitudinal Mechanical Properties (after final heat treatment)
Tensile Strength | Yield Strength | Elongation | Reduction of area |
---|---|---|---|
(0.2% Proof Strength) | |||
MPa | MPa | % | % |
Min | Min | Min | Min |
1793 | 1496 | 10 | 30 |
Transverse Mechanical Properties (after final heat treatment)
Nominal Cross Sectional Area Sq Cms | Tensile Strength MPa | Yield Strength (0.2% Proof Strength) MPa | Reduction of Area % | Reduction of Area % | Elongation % |
---|---|---|---|---|---|
Min | Min | Min (average of all tests) | Min (individual test) | Min | |
645 | 1793 | 1496 | 30 | 25 | 6 |
646 - 929 | 1793 | 1496 | 25 | 20 | 5 |
> 929 | 1793 | 1496 | 20 | 15 | 4 |